Preparation and Study of a Composition Based on Butadiene-Styrene Polymer using Wood Tar

This work is devoted to the topic of preparation and study of a composition based on butadiene-styrene polymer using wood tar.
An optimal recipe for obtaining a rubber mixture using butadiene-styrene rubber and wood tar (which we will sometimes call Kamden in the future) was selected and each component was justified. The rubber mixture was prepared in a mixer located in the laboratory of Bakrezin JSC and the mixing mode was set at a temperature of 1200C for 14 minutes, and the obtained homogeneous dispersed system was cooled to 800C, sulphur and accelerators were added to it. Then the kinetics of the vulcanization process was found. The vulcanization mode was determined as follows: T-1580C, P -12MPa, t - 26 minutes.
The physical and mechanical properties of the vulcanization were studied and it was shown that the indicators of the obtained product meet the requirements of the standard. To determine the durability of these rubber products obtained, the physical and mechanical properties of the vulcanization were determined and the sample had the following characteristics: Tensile strength, 22 MPa, Elongation at break 340%, Residual elongation 12%. Hardness according to TM-2, 85 conventional units.

wooden stone styrene butadiene rubber, modification

1. Alizade Tarlan PHYSICO-MECHANICAL PROPERTIES OF PETROLEUM ROAD BITUMEN MODIFIED ON THE BASIS OF STYRENE-BUTADIENE BUTYL RUBBE, 2024, Innovative scientific research Proceedings of the IX International Scientific and Practical Conference 14-15 March , Pp34-40 DOI: https://doi.org/10.5281/zenodo.10882832 [Google Scholar] [Crossref]

2. Kerem Shixaliyev Research New Ways of Processing Polymer Waste that was Formed as a Result of Operation321-335 Novel Perspectives of Geography, Environment and Earth Sciences Vol. 1 Vol. 1, 22 December 2022 , Page 25-35https://doi.org/10.9734/bpi/npgees/v1/17431D [Google Scholar] [Crossref]

3. Kerem Shixaliyev PROPERTIES OF THE COMPOSITION BASED ON MODIFIED POLYETHYLENES , 2023, Eur. Chem. Bull. , 2023; Volume -12 , Special Issue-5 : Page: 242-258 . doi 10.31838/ECB/2023.12.si5.023 [Google Scholar] [Crossref]

4. Kerem Shixaliyev Study of the Properties of the Composition Obtained Based on Mixtures of Polyvinyl Chloride and Ethylene-Propylene Copolymers International ,2023,Journal of Current Science Research and Review ISSN: 2581-8341 Vol 6 No 1 (2023): Volume 06 Issue 01 January ,pp314-318 doi 10.31838/ECB/2023.12.si5.023 [Google Scholar] [Crossref]

5. Kerem Shixaliyev.Investigating Recycling Methods of End-of-Life Car Tires,2023, Journal of Advanced Zoology, Volume 44 Issue S-3 Year 2023 Page 1149:1157 ,DOI: https://doi.org/10.17762/jaz.v44iS-3.1205 [Google Scholar] [Crossref]

6. Kerem Shixaliyev Investigation of the Рroрerties of a Composition Obtained based on Mixtures of Polyvinylchloride and Synthetic Rubber Ethylene Рroрylene Terрoliymer2023,Editorial Board of Journal of Coastal Life Medicine editor special issue eurchembull . Vol. 11: Number 1, 2023 JCLMM 1/11 pp.|2653–2658, https://www.jclmm.com/index.php/journal/article/view/741. 117-126Technology, DOI: 10.35940/ijitee.G5721.079920 [Google Scholar] [Crossref]

• Green Synthesis of Cobalt Oxide/Gold (Coo/Au) Bimetallic Nanoparticles Using Sinapinic Acid: A Comprehensive Study
• Advances in Solar Cell Technologies: A Comprehensive Review of Material Synthesis, Structural Properties, Efficiency and Diverse Applications
• Thermal Decomposition of Co-Fe-Cr-Citrate Complex Via Structural and Spectral Study
• Surface Activity and Thermodynamic Assessment of Surfactants Derived from Oreochromis Niloticus Oil (Nile Tilapia Fish)
• Green Synthesis of Robust Metal-Organic Frameworks: A Sustainable Approach for Advanced Applications